Hohea Alumina ki te kaha nui, abrasion iti, kahore he fakamolū i te wai, kahore roha, kahore paura me kahore kapiti. Ka taea e whānui te reira i te whakamahi i roto i te whakamaroke hohonu o ngatata hau, ethylene me propylene, hauwai-whakatupuranga, rangi wehenga, mea rangi whakamaroke me te maimoatanga köwhai mo H2O2, ano i roto i te rauemi parahanga rahi, pēnei i H2S, SO2, HF me parawini i roto i te ururua hau, rawa i roto i te defluorinate wai inu.
|
Model |
Alumina Hohea |
|||||
|
Hanga |
poi |
|||||
|
momo |
KA401 |
KA402 |
KA403 |
KA404 |
KA405 |
|
|
Momo Crystal |
XP |
XP |
y |
y |
XP |
|
|
Composition matū |
Ihirangi Al2O3 (%) |
≥93 |
≥93 |
≥93 |
≥93 |
≥93 |
|
Ihirangi Na2O (%) |
≤0.3 |
≤0.3 |
≤0.5 |
0.15-0.3 |
≤0.3 |
|
|
ngā āhuatanga ōkiko |
kiato nuinga (g / ml) |
0.68-0.72 |
0.70-0.75 |
0.65-0.75 |
0.70-0.80 |
0.72-0.78 |
|
rōrahi pore (ml / g) |
0.30-0.45 |
0.30-0.42 |
0.40-0.46 |
0,40 |
0.30-0.50 |
|
|
horahanga mata (m2 / g) |
≥300 |
≥300 |
260-300 |
≥300 |
≥300 |
|
|
Active (%) |
/ |
/ |
56-62 |
/ |
/ |
|
|
mate takanga (%) |
≤1.0 |
≤1.0 |
≤1.0 |
≤0.4 |
≤0.8 |
|
|
Loi (%) |
≤8 |
≤8 |
≤8 |
≤5 |
≤8 |
|
|
absorption Static (%) (RH = 60%) |
Water absorption |
köwhai absorption |
Water absorption |
Water absorption |
Water absorption |
|
|
17-19 |
0.2-0.3 |
50 |
50-70 |
17-19 |
||
|
Kuru kaha (N / PC) |
Φ1-2 (mm) |
≥40 |
≥40 |
/ |
/ |
/ |
|
Φ2-3 (mm) |
≥70 |
≥70 |
/ |
/ |
/ |
|
|
Φ3-5 (mm) |
≥120 |
/ |
≥120 |
≥120 |
≥120 |
|
|
Φ4-6 (mm) |
≥150 |
/ |
≥150 |
≥150 |
≥150 |
|
|
Φ5-7 (mm) |
≥200 |
/ |
/ |
/ |
≥200 |
|
|
Φ6-8 (mm) |
≥300 |
/ |
/ |
/ |
≥300 |
|
|
Φ12-14 (mm) |
≥350 |
/ |
/ |
/ |
/ |
|